Powdered coating composition of unsaturated aycidyl polymer containing a sulfur terminating group, dicarboxylic acid, polester and polyacrylate

ABSTRACT

Thermosettable coating powders comprising solid, low molecular weight, storable epoxy-functional acrylic terpolymers of glycidyl methacrylate, a lower alkyl acrylate and methyl methacrylate together with crosslinking agents, plasticizers and surfactants therefor.

United States Patent [1 1 lackley et al.

[4 1 Dec. 31, 1974 POWDERED COATING COMPOSITION OF UNSATURATED AYCIDYL POLYMER CONTAINING A SULFUR TERMINATING GROUP, DICARBOXYLIC ACID, POLESTER AND POLYACRYLATE Inventors: William D. Blackley, Afton Township, Washington County; Richard B. Castle, Woodbury; Leslie G. Berntson, Richfield, all of Minn.

Assignee: Minnesota Mining and Manufacturing Company, St. Paul, Minn.

Filed: Feb. 2, 1973 Appl. No.: 329,090

US. Cl 260/835, 260/31.6, 260/79.5 NV, 260/80.72, 260/836, 117/16, 117/17, 117/21,

Int. Cl C08g 30/12, C08g 45/04 Field of Search 260/836, 835, 80.72, 31.6, 260/79.5 NV; 117/21, 132 BE Primary ExaminerMurray Tillman Assistant Examiner-J. Ziegler Attorney, Agent, or Firm-Alexander, Sell, Steldt DeLal-lunt [5 7 ABSTRACT Thermosettable coating powders comprising solid, low molecular weight, 'storable epoxy-functional acrylic terpolymers of glycidyl methacrylate, a lower alkyl acrylate and methyl methacrylate together with crosslinking agents, plasticizers and surfactants therefor.

4 Claims, No Drawings POWDERED COATING COMPOSITION OF UNSATURATED AYCIDYL POLYMER CONTAINING A SULFUR TERMINATING GROUP, DICARBOXYLIC ACID, POLESTER AND POLYACRYLATE SUMMARY OF THE INVENTION This invention relates to thermosettable coating pow- I BACKGROUND OF THE INVENTION The powder coating technique in general involves application of a finely divided organic powder to an article and the subsequent conversion of the powder through application of heat to an adherent continuous coating. It is particularly well suited to modern assembly line oper'ation,,especially when protective and/or decorative coatings are to be applied to metal articles. The organic powder is applied to the article by one of the known methods, such as the fluidized bed and electrostatic spray methods, and then heated to cause it to fuse and flow into a continuous coating on the article being coated and to subsequently become thermoset. The thermoset coatings resulting from these powders are tough, solvent resistant and weather resistant. Unless pigments, dyes or other such materials are added, they are clear and highly glossy.

Thermosetting powder coatings have certain recog nized advantages, both in the coating process and in the properties of the final coating. Thus, no solvent or primer is needed, single coat coverage is possible and there no sagging of the film. Also, there is often an improved hardness-flexibility relationship and the films have more universal chemical and solvent resistance.

Among the classses ofthermosetting coating powders are those based on epoxy, polyester and acrylic systems. These may be combined and/or modified, e.g., epoxy-acrylic and polyester-acrylic systems can be used. They can also be modified with other crosslinking components such as unsaturates and aminoplasts. More extensive information relative to the thermosetting powder coating field is provided in the review entitled Thermosetting Polyester and Acrylic Powder Coatings," D. D. Taft, R. Hong and W. J. McKillip, publication number FC 72-942 of the Society of Manufacturing Engineers, 20501 Ford Road, Dearborn, Mich.,

One economically important difficulty with powder coated surfaces is an aesthetic one, i.e., their characteristic orange peel appearance. This is caused by their characteristic surface configuration which gives an appearance similar to that of the peeling of an orange. Agents which have been used in the past to reduce the orange peel have had the additional effect ofincreasing the blocking" of the powder (i.e., the tendency of the particles to agglomerate, resulting in failure ofthe powder to flow freely and thereby make coating difficult or impossible). Thus, attempts to alleviate one serious problem in powder coatings has brought on another problem which has been perhaps, more serious.

THE PRESENT INVENTION The present invention relates to a class of thermosettable coating powders which are easily ground into powder form, being relatively brittle at ambienttemperature, are stable during storage as powders (i.e., are free from blocking), undergo substantial flow on fusion to form a continuous coating and, upon continued application of heat, convert to tough, adherent, solvent resistant coatings. Thus, the powder coating compositions are easily used and form strongly adhering weatherable, solvent resistant coatings. They contain a basic polymer and a particular compounding system therefor which, in combination, provide the desired properties.

More particularly, the coating powders comprise 1. 100 parts ofa solid, low molecular weight, substantially linear, storable epoxy-functional acrylic terpolymer of 5-20 parts glycidyl methacrylate units, 5-35 parts oflower alkyl acrylate units in which the alkyl group contains from two to four carbon atoms, 5070 parts of methyl methacrylate units, and 05-10 parts of chain terminating-groups selected from wherein R is an alkyl group containing not more than 20 carbon atoms, said terpolymer'having a. a glass transition temperature of from20 to b. a Durrans melting point of from to 170 Cf c. a melt index of from 1 to 30, at a temperature of 152 C. with a piston loading of 1,200 grams and an extrusion orifice of 0.0465 inches, and

d. an epoxy equivalent weight of 700-3,000 grams per epoxy group.

2. 0-20 parts of a crosslinking agent selected from saturated aliphatic dicarboxylic acids having from 5 to 20 carbon atoms which is essentially unreactive at room temperature but which reacts rapidly above 150 C.

3. 0-40 parts of an acid-terminated linear polyester plasticizer-curative (or plasticizer-crosslinking agent)having an equivalent weight per carboxyl group of from to 1,500 and 4. 0.1 to Sparts ofa non-ionic aliphatic poly acrylate.

surface active agent, provided that the ratio of total carboxyl equivalence of (2) plus (3) is 0.5-1.5:1 of the epoxy equivalence of (l).

In the compositions to be used in applications in which particularly smooth coating surfaces are desired (which are free of orange peel) it is also advantageous to add, as a surface leveling agent, l-l0 parts (based on 100 parts of terpolymer) of glyceryl tris( l2- hydroxystearate). This compound is a hydrogenated castor oil having an hydroxyl equivalent weight of about 185. It is a wax with a melting point of from about 84 to 87 C. and an iodine value of 3-6 and is available from the Baker Castor Oil Company of Baacrylate. The lower alkyl acrylate is ordinarily ethyl acrylate.

The glass transition temperature is that temperature range at which an amorphous polymer changes from a brittle glassy state to a flexible rubbery state. This has been characterized in the terpolymers herein by the temperatures at which the material exhibitsa discontinuous change in heat capacity as measured by differential thermal analysis. The melting point measurements herein were made by the Durrans mercury method and the melt index measurements were made according to ASSTM-Dl238 at a temperature of 152C, a piston loading of 1200 grams and an extrusion orifice of 0.0465 inches.

The terpolymers are prepared by agitating in an inert atmosphere I. an aqueous medium containing a suspending aid,

2. a monomer charge of 5-20 parts of glycidyl methacrylate, 5-35 parts of a lower alkyl acrylate in which the alkyl group contains from 2 to 4 carbon atoms and 5070 parts of methyl methacrylate,-

3. 0.5l parts of a chain transfer agent of the formula s ROt'iCHzSH or (It-092$ wherein each R is an alkyl group containing not more than 20 carbon atoms, and 4. 005-5 parts of a free radical initiator, at from.60

to 90 C. for not less than two hours. Thus, the preparation of the polymers is carried out in the absence ofa solvent for the polymer by a suspen- I sion polymerization technique. Preferably. a mixture of the monomers, the chain transfer agent and the initiator is added to a heated, stirred, aqueous solution of the suspending agent under an inert (e.g., nitrogen) atmosphere. After the addition is complete, the agitation and heating are maintained for not less than two hours and ordinarily for not more than hours. The polymer is recovered by cooling the mixture, filtering, washing and drying. The resulting product is free-flowing polymer beads, suitable for subsequent processing. Alternatively, the initiator may be suspended in the aqueous phase and the monomer mixture added in small increments. This process results in the preparation of a relatively low molecular weight terpolymer with substantially complete conversion ofthe monomers charged to polymer. The suspension polymerization technique of this process avoids the substantial loss oflow molecular weight components of polymer (often characteristic of the isolation step in solution polymerizations which involve the precipitation of the polymer from solution by means of a non-solvent). The retention in the product of the low molecular weight components, furthermore, is advantageous in that it aids in the thermal flow of the polymer in the fusion step of the powder coating operation.

As noted previously, the terpolymers have a melt index within a particular range. In order to control this, and the molecular weight of the polymer, particular chain transfer agents are used, i.e., compounds of the formulae wherein each R is an alkyl group containing not more than 20 carbon atoms. The uses of these chain terminating agents result respectively in chain terminating groups of the formulae ll ll ROCCHzS and ROCS- wherein R is as previously defined. These particular classes of chain transfer agents have been found to be particularly useful since they not only control the molecular weight (and hence the melt index) ofthe' resulting polymer to the desired degree but also they do not inhibit the complete conversion of monomers to polymer. When commonly used chain transfer agents. such as lauryl or dodecyl mercaptan, are used at sufficient levels to produce a polymer having the desired melt index, a product with an unacceptableamount of residual monomer is produced. To reduce the amount of monomer in the product to an acceptable level, up to l() percent by weight ofinitiator may be required. In the practice of the present process, however, using the preferred chain transfer agent, relatively low levels of initiator are sufficient for substantially percent conversion of monomers to polymer.

Preferably in the chain transfer agents of the type 0' aot iolr sn,

R is isooctyl. Such compounds in which R contains fewer than five carbon atoms are less effective and those in which R contains more than eleven carbon atoms appear to be deleterious of suspension stability. In the chain transfer agents of the type s ll -oo s, W (R /2 R is preferably R'CH whereinR' is hydrogen or an alkyl group bonded to the CH through a tertiary carbon atom (e.g., R is ter t-butyl). The reason for this is that polymers made using chain transfer agents of the second type,

in which R is a group bearing hydrogen on the B carbon atom are thermally unstable.

Suitable free radical initiators for use in the process ofthe invention are, for example, peresters, acyl peroxides, and azo compounds. Specifically these include benzoyl peroxide, lauroyl peroxide, t-butyl perbenzoate, t-butyl peroxypivalate, dibenzyl peroxydicarbonate, diisopropyl peroxydica rbonate and azobis isobutyronitrile, ultraviolet light or ionizing radiation.

Either ionic suspending aids, such as poly(sodium acrylate) or poly(ammonium acrylate) or non-ionic aids such as poly(vinyl alcohols) are suitable.

The crosslinking agents and plasticizer-curatives (i.e. plasticizer-crosslinking agents) used in the thermosetting coating powders are polycarboxylic (preferably dicarboxylic) or anhydride (preferably monoanhydride) type materials, ordinarily selected from the polycarboxylic acids and anhydrides themselves and acidterminated polyesters thereof. The ratio of the total carboxyl equivalency of these materials (constituents (2) and (3) of the coating powders) to the epoxy equivalence the terpolymer is 0.5-1.5:1.

Each anhydride group is considered to be equivalent to two carboxyl groups with respect to this ratio. The polycarboxylic acids and anhydrides can be aliphatic (e.g., alkanoic) or aromatic in nature and ordinarily contain from five to 20 carbon atoms.

The acid-terminated polyesters are useful for introducing flexibility into the cured coatings (plasticizing them) and for preventing chipping and flaking of the coatings, due to their longer chains. It is frequently preferred to utilize a mixture of crosslinking agents and plasticizer-curatives, ordinarily one of each. A particularly preferred crosslinking-plasticizing system is -20 parts of an acid terminated butanediol adipate having an acid equivalent weight of 500-1 .000 combined with an alkanoic dicarboxylic acid containing from five to 20 carbon atoms, so that the ratio of the totalcarboxylic acid equivalence is 0.9-1 .1:l of the epoxy equivalence of the terpolymer.

The surface active agents provide good substrate wetting. When no surface active agent is present, the molten coating often does not wet the substrate surface sufficiently to give an optimum uniform coating and small imperfections (pocks) form in which the coating is very thin. These pocks are effectively eliminated by adding 0.1- parts, preferably 0.21.5 parts, based on 100 parts of terpolymer, of a non-ionic aliphatic polyacrylate surface active agent. This can be an aliphatic polyacrylate, such as poly(Z-ethylhexylacrylate)'.

Although the powder coating compositions can be used without catalysts, it is preferred that a catalyst be included to facilitate the crosslinking reaction and thus enhance the solvent resistance and abrasion resistance of the resulting coating. The higher rate of reaction brought about by the catalyst is also an'advantage. The catalysts are advantageously used in amounts varying from about 0.05-2 parts (based on 100 parts ofterpolymer). They are of the types which promote the acidepoxy crosslinking reaction and/or promote the epoxyepoxy polyetherification cross-linking reaction. The amount of catalyst used will vary with the specific crosslinking agent and its concentration as well as the specific time and temperatures used in the sinteringthermosetting coating process. The catalysts which are used do not significantly enhance the rate of reaction at room temperature (that is to say they are latent at that temperature) but become active at particular selected higher temperatures. The catalysts that are latent up to at least 50C. are preferred. Catalysts for the epoxy-carboxylic reaction are useful in the coating powders of the invention provided, most preferably, that they can be incorporated into the powder without causing blocking over a period of six months at 50C., and provided further that they do not cause foaming during the curing cycle.

Useful catalysts include heavy metal salts of organic acids (ordinarily those containing from 2 to 22 carbon atoms) such as stannous carboxylic acid salts including stannous octoate and stannous stearate,'tertiary or qua- Additionally, up to about 60 percent by weight ofthe coating powder of one or more additives such as pigments, dyes, fillers (inorganic or organic), metallic flakes, ultraviolet absorbers, etc., can be added to the powders. Thus, fillers or extenders such as mica, silica, calcium carbonate, barytes, etc. can be used to increase the hardness and/or reduce the costs of the finished products. Pigments or dyes, such as phthalocyanine blue, titanium dioxide, chromium oxide, carbon black, and the acrylamide yellows or oranges, etc., may be incorporated into the coating powders for the purpose of coloring or opacifying the resulting coatings. Metallic flakes such asaluminum may be incorporated into the coating powders to lend decorative effects to the resultant coatings.

The thermosettable coating powders are prepared by dissolving or thoroughly dispersing all of the constituents in a suitable solvent. These include ketones, esters, aromatic hydrocarbons, chlorinated hydrocarbons and ethers, which are readily removed by distillation Among the preferred solvents are acetone, ethyl acetate, benzene, tetrahydrofuran and methylene chloride. Once the constituents are thoroughly mixed, the solvent is evaporated under vacuum, leaving a solid cake which is crushed into a fine powder. Alternatively, the coating powder can be prepared by mixing the powdered constituents together and homogenizing the mixture by processing it through a mixing extruderor on a two roll mill and grinding to less than micron par ticle size powder.

The following examples are given for the purpose of further illustrating the present invention, but are not intended, in any way, to be limiting on the scope thereof. All temperatures herein are given in degrees Centigrade and the parts are expressed by weight.

TERPOLYMER PREPARATION EXAMPLE 1 A mixture of 62.4 parts (423 grams) of methyl methacrylate, 24.0 parts (163 grams) of ethyl acrylate, 13.6 parts (92 grams) of glycidyl methacrylate, 3.9 parts (26.5 grams) of isooctyl mercaptoacetate ll (R10 C CHzSI-I of 28. The epoxy equivalent weight was found to be 1199 as compared to a calculated value of 1127.

EXAMPLE 2 I To 225 parts of a stirred 0.1 percent aqueous solution of poly(sodium acrylate) at a temperature of 68 was added a mixture composed of 62 parts of methyl methacrylate, 24 parts of ethyl acrylate, 14 parts of glycidyl methacrylate, 3.9 .parts of isooctyl mercaptoacetate and 3.5 parts of benzoyl peroxide. The reaction temperature dropped to 60 and was held there, with stirring for 5 hours. The mixture was cooled and filtered, the solids washed with water and dried to give 93 percent of the theoretical amount of polymer beads with l a melt index of 2.2. a melting point of 154, an epoxy equivalent weight of 1,262 and a glass transition temperature of 41.

EXAMPLE 3 The polymerization was carried out as in Example 2 Monomers:

MMA=Met11yl methaerylate EA= Ethyl acrylate GMA Glyeidyl methacrylute suspending agents:

PVA=Po1y(vinyl alcohol) P (N M.) Po1y(s0dium acrylate) Chain transler agents:

IOM =Isooety1 mereaptoacetate nBuM =n-Buty1 mercaptoacetate Dodee M dodecyl mereaptoacetate Free radical initiators:

BPO =Benzoy1 peroxide AIBN =Azobisisobutyronitri1e =Dineopeutyl dixanthogen Aqueous phase Monomers Susp. 3

agent Chain transfer agent Free radical initiator Parts Parts Parts and Example No. MMA EA GMA concn. Parts Agent Parts Initiator Parts 8 .1 67 19 14 0.2% 250.1OM 4.0 AIBN 0.16

' PVA 50 34 7 0.1% 350 IOM 3.0 BIO 1.4

, P(NaA) 10 52- 2s 0.1% 330 IOM 2.4 BPO 1.1

P(NaA) 11 02 24 14 0.1% 250 10M 3.9 BPO 3.5

P(NaA) 12 s2 24 14 0.2% 240 10M 3.9 AIBN 0.10

PVA 13 62 24 14 0.2% 310 IOM 2.9 AIBN 0.4

PVA

14 G2 24 14 0.2% 310 3.1 BPO 1.2

PVA ll (CH3OCS) 15 62 24 14 0.2% 310 v S I 4.7 BPO 1.2

PVA 11 (CHa) C-CH2OCS 2 16 62 24 14 0.1% 310 nBuM 2.8 BPO 2.3

PVA

17 02 24 14 0.1% 310 Dotlec M 3.7 BPO 1.2

P(NaA) Aqueous phase described in terms of the concentration of the particular suspending agent in the resulting polymer.

EXAMPLES 4-7 Four additional polymer lots according to the invention were prepared using the procedure of Example 1.

The first three (Examples 4-6) were run in 300 gallon kettles, utilizing 700 pound monomer charges and the fourth (Example 7) was run in 2150 gallon kettle utilizing a 115 pound monomer charge. The physical properties of the resulting polymers were as follows:

Example Melting Melt Epoxy Eq. No. Point C index Tg "C Weight EXAMPLES 8-17 Time & Example Durrans Melt Epoxy Temp.

No. m.p.. lndex Tg.C Equivalent of C Weight Polymn.

8 130 5.2 49 1105 4 hrs 9 123 10.2 33 2205 2 hrs 80 and 2 hrs 10 135 1.4 42 805 3 hrs 80 11 134 5.3 28 1199 5 hrs 60 12 117 14.1 29 1205 4 hrs 80 13 126 5.4 50 1265 5 hrs 80 14 130 8.6 1362 2 hrs 80 and 3 hrs 90 15 134 4.6 1250 2 hrs 80 and 3 hrs 90 16 143 26 1315 2 hrs 80 and 3 hrs 90 17 134 6.0 1232 2 hrs 80 and 3 hrs 90 EXAMPLE 18 of 0.1 percent aqueous p01y(s0dium acrylate) at 60 under a nitrogen atmosphere. The mixture was stirred for 3 hours at 80 then cooled, filtered, washed, and dried.

The resulting polymer had a melt index of 2.3, a melting point of 165 and an epoxy equivalent weight of 1,189 but contained 17 percent of volatiles (residual monomer). This illustrated the disadvantage of using dodecyl mercaptan as a chain transfer agent.

THE THERMOSETTING COATING POWDER FORMULATlONS EXAMPLE 19 The following were blended on a 6 inch two roll rubber mill:

Terpolymer of Example 3 Poly Z-ethyl hexyl acrylate (Modaflow;

available from Monsanto) Butanediol adipate (1) Glyceryl tris l Z-hydroxy stearate) (2) Titanium dioxide pigment Black pigment Stannous stcarate (l) Acid terminated butanediol adipate with an acid equivalent weight of 815.

(I) ailahle from The Baker Castor Oil Co.. BZQUHHC. NJ. under the trade dc ignznion Castorwax".

onto

passed through the 230 mesh screen was then electro.-

statically sprayed at room temperature onto a metal test panel (surface treated cold rolled 20 gauge steel panel with a zinc phosphate surface treatment designated Bonderite 40 and available from the Parker Co. Detroit, Mich.) and the coated panel was cured 20 minutes at 177C. in a forced air oven.

The resulting gray colored coating was superior to known acrylic powder coatings in gloss, lack of orange peel, flexibility and weathering. It also passed-an MEK rub test, resisted exposure to a day salt spray test and passed a 180 bend test without cracking. Other colors were readily prepared by replacing the black and white pigments with pigments of other colors.

The MEK rub test consists of 30 circular wipes at light hand pressure with a pad of 50 grade cheese cloth saturated with methyl ethyl ketone. In order to pass this test the coating must not be scratched or removed, ei-

ther by disappearance of the film from the steel panel or by color transfer to the pad. The salt spray test is designated ASTM B117. In the 180 bend test, a Q panel (a standard test panel approximately 4 to 8 inches of untreated gauge cold rolled steel conforming to ASTM specification A 109) was coated to a thickness of approximately 2 mils and a corner was slowly bent 180. The bend was inspected for cracking, chipping or flaking.

EXAMPLE 20 The following systems were prepared, coated and cured as in Example 19 then evaluated to demonstrate the beneficial effect of the acid terminated butanediol adipate.

A B C D Terpolymer of Example 3 100 100 100 Poly 2-ethyl hexyl acrylate 1.5 1.5 1.5 1.5 Glyceryl tris (12- hydroxy stearate) 5.0 5.0 5.0 5,0 Sebacic acid 8.4 8.2 8.0 7.9 Butanediol adipate I (as in Example 19) O 1.7 3.3 5.0 Black pigment 2.3 2.3 2.3 2.3 Stannous stearate .084 .084 .084 .084

The incorporation of the butanediol adipate made the coating more flexible and impact resistent. Thus, the coated panels were subjected to a 50 pound impact test (ASTM 2794-69) and assigned ratings on the following basis Rating 1. No cracking 2. Slight cracking 3. Considerable cracking 4. Extensive cracking with flaking The panels were rated as follows:

Formulation No. Rating A v 3 B 3-4 C 2-3 D 2 EXAMPLE 21 The systems of this example were prepared, coated and cured as in Example 19 then evaluated to demonstrate the effect of the melt index of the terpolymer on the resulting coatings.

Melt Index Terpolymer of 100 Example 4 Terpolymer of 10.1 100 Terpolymer of Example 6 Poly 2-ethyl hexyl acrylate Sebacic acid Butanediol adipate (as in Example 19) Glyceryl tris (lZhydroxy stearate) 3.3 3.3 Black pigment 0.42 0.42 Titanium dioxide pigment The coating of Lot B exhibited the least orange peel, Lot C was intermediate and Lot A the most orange peel.

EXAMPLE 22 The following samples were made and evaluated in the mannerdescribed in Example 19 to demonstrate the use of diacids as crosslinking agents.

Components A B C D Terpolymer of Example 3 100 100 100 100 Poly 2-ethyl hexyl acrylate 2.0 .0 2.0 ".0 (ilyccryl Iris (12' hydroxy slearalcl 5.0 5.0 5.0 5.0 Dndccanetlioic acid 7.5 Axlipic acid 5.17 Azclaic acid 6.67 Scbacic acid 7.17 BUillllCtilOl adipatc (as in Example 19) 10.0 10.0 10.0 10.0 Black pigment 2.5' 2.5 2.5 2.5 Stannous stearate .084 .084 .084 .084 Tests 180 Bend pass pass pass pass Gel time of powder (sec.) 35 35 35 37 Solvent Ruh (MEK) pass pass pass pass The rate and degree of cure could be controlled by 20 EXAMPLE the addition of catalysts such as, stannous stearate, The following lots of thermosetting coating powders stannous ogtoate methyl lmldazoles' demonstrate the effects of glyceryl tris (12- The ben and so vent rub tests are described heremhydroxystearate) in the coating powders above. The gel time test 15 run as follows: A sample of powder is placed on a surface heated to 204C.'and the 5 time required to reach a rubbery state is determined by stirring'the molten resin and determining the point at Y which it becomes viscous and stringy. This time is re- A Lot}; corded as the gel time. 7

. Terpolymer of Example 3 I00 I00 EXAMPLE 23 Poly 2-ethy1hexylacry1ale 1.5 1.5 l Butanediol adipate as in A thermosettmg coatmg powder containing only ter- Example 19 10.0 10.0 polymer, cross linking agent and surface active agent z' g 0 33 was prepared by dissolving 100 parts of the terpolymer se'bacic acid 1 m of Example 2, 0.49 parts of poly 2-ethyl hexyl acrylate 35 sl a Swarm 3 g: 32g

Bac pigment and 667 parts of adiprc acid in 140 parts of tetrahydro Titanium dioxide pigment 473 47,8

furan at room temperature. The tetrahydrofuran was removed using a rotary evaporator and the remaining resinous composition was pulverized and dried overnight in a vacuum at room temperature. Thedried'mixture was then micropulverized and screened to collect the material less than 53 mu in size.

The powdered composition obtained was electrostatically-coated onto steel panels and cured at 177C. for 20 minutes. The resulting finish was a clear, glossy and transparent coating which was much moreresistant to breaking on bend. than a similar panel cured at 177C. for 3 minutes. This indicates the thermosetting nature of such compositions.

EXAMPLE 24 The following lot demonstrates the use of a high catalyst level.

Terpolymer of Example 2 I00 Poly Z-ethyl hexyl acrylate 1.0 Adipic acid 4.3 Butanediol adipate (as in Example 19) 20 Titanium dioxide pigment 31 DOBP 2.0

Slannous stearatc The above powdered coating system had a gel time of 26 seconds and gave a 60 gloss reading of 84 when sprayed onto a test panel and cured. The 60 gloss test conforms to ASTM D-l47l-57T.

These systems were prepared, coated and cured as in Example 19. There was no blocking of the powder in either lot. The final coating of Lot B was much better than the comparable coating (of equal thickness) of Lot A with respect to orange peel, i.e., the coating of Lot B had much less orange peel than that of Lot A.

Preferably the coating powder compositions of the invention contain 5-20 parts-of (2) and 5-40 parts of (3), based on parts of I the terpolymer.

A particularly preferredclass of compositions of the invention are those comprising 1. a solid, low molecular weight, substantially linear, storable epoxy-functional acrylic terpolymer of 13-14 parts glycidyl methacrylate units, 23-24 parts of ethyl acrylate units, 59-60 parts of methyl methacrylate units and 3-4 parts of chain terminating groups of the formula nodomswherein R is an isooctyl group, said terpolymer having a. a glass transition temperature of from 30 to C.,

b. a Durrans melting point of from to C.,

c. a melt index of from to 20, at a temperature of 152 C., with a piston loading of 1,200 grams and an extrusion orifice of 0.0465 inches, and d. an epoxy equivalent weight of 1,100-1,300,

2. 7-8 parts of an aliphatic dicarboxylic acid containing 9-10 carbon atoms, (azelaic acid and sebacic acid),

3. 8-12 parts ofbutanediol adipate having an equivalent weight per carboxyl group of 500-1000, and

4. 1-2 parts of poly 2-ethyl hexyl acrylate.

What is claimed is:

l. A thermosetting coating powder comprising 1. 100 parts of a solid, low molecular weight, substantially linear storable epoxy-functional acrylic terpolymer of 5-20' parts of glycidyl methacrylate units, 5-35 parts of lower alkyl acrylate units in which the alkyl group contains from two to four carbon atoms, 50-70 parts of methyl methacrylate units, and 0.5-10 parts ofchain terminating groups selected from wherein R is an alkyl group containing not more than I carbon atoms and R" is hydrogen or'an alkyl group bonded to the CH group in the formula through a tertiary carbon atom, R containing not more than 19 carbon atoms, said terpolymer hava. a glass transition b. a Durrans melting point of from 90 to 170 c.

c. a melt index of from 1 to 30, at a temperature of 152 C. with a piston loading of 1,200'grams and an extrusion orifice of 0.0456 inches, and

d. an epoxy equivalent weight of'700-3,000 grams per epoxy group 2. 5-20 parts of a crosslinking agent selected from saturated aliphatic dicarboxylic acids having from 5 to 20 carbon atoms which is essentially unreacternperature of from 20 to 70 tive at room temperature but which reacts rapidly above 150 C.

3. 5-40 parts of an acid-terminated linear polyester plasticizer-curative having an equivalent weight per carboxyl group of from to 1,500 and 4. 0.1 to 5 parts ofa non-ionic aliphatic polyacrylate surface active agent, 7

provided that the ratio of total carboxyl equivalence of (2) plus (3) is 0.5-1.5:1 ofthe epoxy equivalence of l 2. A thermosetting coating powder according to claim 1 wherein the lower alkyl acrylate is ethyl acrylate.

3. A thermosetting coating powder according to claim 1 wherein the terpolymer contains 10-15 parts of glycidyl methacrylate, 20-25 parts oflower alkyl acrylate units and 60-65 parts of methyl methacrylate units.

4. A thermosetting coating powder comprising 1. 100 parts of a solid, low molecular weight, substantially linear, storable epoxy-functional acrylic terpolymer of 13-14 parts glycidyl methacrylate units, 23-24 parts of ethyl acrylate units, 59-60 parts of methyl methacrylate units and 3-4 parts of chaim terminating groups of the formula ll ROCCH2S- wherein R is an isooctyl group, said terpolymer havmg a. a glass transition temperature of from 30 to 60 C., b. a Durrans melting point of from to C., c. a melt index of from 5 to 20, at a temperature of 152 C., with a piston loading of 1,200 grams and an extrusion orifice of 0.0465 inches, and d. an epoxy equivalent weight of 1,100-1,300, 2. 7-8 parts of an aliphatic dicarboxylic acid containing 9-10 carbon atoms, 3.'8-12 parts of butanediol adipate having an equivalent weight per carboxyl group of 500-l,000,and 4, 1-2 parts of poly 2-ethyl hexyl acrylate. 

1. A THERMOSETTING COATING POWDER COMPRISING
 1. 100 PARTS OF A SOLID, LOW MOLECULAR WEIGHT, SUBSTANTIALLY LINEAR, STORABLE EPOXY-FUNCTIONAL ACRYLIC TERPOLYMER OF 5-20 PARTS OF GLYCIDYL METHACRYLATE UNITS, 5-35 PARTS OF LOWER ALKYL ACRYLATE UNITS IN WHICH THE ALKYL GROUP CONTAINS FROM TWO TO FOUR CARBON ATOMS, 50-70 PARTS OF METHYL METHACRYLATE UNITS, AND 0.5-10 PART OF CHAIN TERMINATING GROUPS SELECTED FROM
 2. 5-20 parts of a crosslinking agent selected from saturated aliphatic dicarboxylic acids having from 5 to 20 carbon atoms which is essentially unreactive at room temperature but which reacts rapidly above 150* C.
 2. A thermosetting coating powder according to claim 1 wherein the lower alkyl acrylate is ethyl acrylate.
 2. 7-8 parts of an aliphatic dicarboxylic acid containing 9-10 carbon atoms,
 3. 8-12 parts of butanediol adipate having an equivalent weight per carboxyl group of 500-1,000,and
 3. A thermosetting coating powder according to claim 1 wherein the terpolymer contains 10-15 parts of glycidyl methacrylate, 20-25 parts of lower alkyl acrylate units and 60-65 parts of methyl methacrylate units.
 3. 5-40 parts of an acid-terminated linear polyester plasticizer-curative having an equivalent weight per carboxyl group of from 100 to 1,500 and
 4. 0.1 to 5 parts of a non-ionic aliphatic polyacrylate surface active agent, provided that the ratio of total carboxyl equivalence of (2) plus (3) is 0.5-1.5:1 of the epoxy equivalence of (1).
 4. A thermosetting coating powder comprising
 4. 1-2 parts of poly 2-ethyl hexyl acrylate. 